In material science, amorphous is a solid whose internal microstructure lacking of long-range order that is characteristic of a crystal.
Amorphous is also called metallic glass.
After metal becomes amorphous, a subsequent heat treatment transforms the initially amorphous microstructure into new form in which fine crystalline grains (average grain diameter of 10-40 nm) embedded in an amorphous residual phase. The new form is called nanocrystalline.
SUNBOW’s iron-based amorphous alloy-SWAM is a product series which are universal solutions in many aspects to commonly use ferrite, silicon steel and iron powder materials, such as: power transformer, inductor, reactor, rotor & stator...
SUNBOW’s iron-based nanocrystalline alloy-SWNA is a product series which are excellent solutions to current transformer (high-precision for electricity meter, high-voltage for substation, and zero-sequence for leakage protection), high-frequency power transformer, and common mode choke (CMC) ...
Â
Â
SUNBOW’s amorphous-SWAM & nanocrystalline-SWNA alloys are based on Fe, Si, B and with further additions of Nb and Cu, and produced by rapid solidification technology.
Composition metals melt in furnace under around 1500℃, and turn into liquid metal which pass through a narrow nozzle, and solidify at a rate of approximately 1million degrees/s. Atoms have no enough time to reach microstructure-crystalline state and stay in amorphous state.
A subsequent heat treatment-annealing at around 500~600℃ transforms the initially amorphous microstructure into nanocrystalline state in which fine crystalline grains (average grain diameter of 10-40 nm) embedded in an amorphous residual phase.
Â
Fig.1 Rapid solidification technology to produce thin metal ribbons with amorphous structure.
Fig.2 Crystalline
Amorphous
Nanocrystalline
Â
Â
• The below characteristics of the iron-based amorphous alloys lead to ultra low core loss.
Thinner thickness —1/10 of CRGO;
Higher electrical resistance — two times higher than CRGO;
Lower coercive force —1/3 of CRGO.
• The magnetic devices made with iron-based amorphous alloy could be operated at higher working induction with excellent anti-saturate ability and smaller size, due to the highest saturation induction among all amorphous alloys.
• 3 tailored products of low core loss, excellent overload tolerance, and high saturation could be provided, according to customer’s different requirements.
Â
Â
SWAM
RIBBON MATERIAL
Â
Composition
Fe: 80%, Si: 9%, B: Balance
Â
Main Properties
Low coercivity-2.4 A/m Very high electrical resistivity-1.3 μΩ.m
Â
Applications
Power Transformer, High Speed Motor, Welding Machine, Medical Equipment (X-ray, CT, Nano-Knife)…
Â
Magnetic Properties (typical values)
Coercivity |
2.4 |
A/m |
Curie temperature |
410 |
℃ |
Saturation flux density |
1.56 |
T |
Maximum permeability |
200,000 |
 |
Initial permeability |
1,000 |
 |
Saturation magnetostriction |
20~30 |
ppm |
Â
Static virgin curve (typical values)
Magnetic field strength |
H (A/m) |
3 |
100 |
500 |
1000 |
2000 |
3000 |
Induction |
B (T) |
0.6 |
0.7 |
0.75 |
1.2 |
1.5 |
1.56 |
Â
Iron Loss-B=0.1T (typical values)
Thickness |
d (mm) |
24 |
24 |
24 |
24 |
24 |
24 |
Frequency |
f (KHz) |
1.5 |
5.0 |
10 |
50 |
80 |
100 |
Loss |
p (W/kg) |
0.2 |
0.9 |
2.3 |
20 |
37 |
50 |
Â
Physical Property
Density |
7.2 |
g/cm3 |
Electrical resistivity |
1.3 |
μΩ.m |
Thermal expansional |
4.7 |
ppm/℃ |
Crystallization temperature |
535 |
℃ |
Â
Form (soft & bendable)
·Cold-rolled: |
Thickness=18~30μm |
Width=142/170/213mm |
·Slitting-strip: |
Thickness=18~30μm |
Width=5~80mm |
Â
Important Note:
Specific magnetic properties could be induced by a heat treatment process.
To achieve optimum properties, a final annealing is indispensable!
Â
Â
Q: Are you trading company or manufacturer?
A: We are professional manufacturer specialized in the designã€development and production of new-type amorphousã€nanocrystallineã€silicon steel sheets and other magnetic materials and components.
Â
Q: What’s your production capacity?
A: The annual production capacity of amorphous&nanocrystalline ribbon is 600 tons;
The annual production capacity of power electronic core is 35 million;
C-type iron core annual production capacity of 240 tons;
The annual production capacity of reactors is 50,000;
Â
Â
Â
Â
1. Tell us what you need,you can call 021-63306968
Or send email to :sales@sunbowgroup.com
We supply nanocrystaline Soft Magnetic Material &Amorphous Soft Magnetic Material , please advise your request information:
1. Material Type
2. Application - Current Transformer, CMC, Audio, etc.?
3. Strips Width
4. Srips Thickness-- µm?
5. Potential Quantity -- kg?
Â
2. Get solution & quote
We will work on the best solution and provide primarily specification& quote for your review.
Â
3. Sample production and mass production
We will start mass production after customer confirmation and validation of samples.
Â
Â
Â
Â
Â
Â
Â
Â
Â
Â
Â
Â
Â
http://www.sunbowmagnetic.com/